Type 310S Stainless Steel is identical to Type 310 except for a lower carbon content that minimizes carbide precipitation and improves weldability. They are essentially nonmagnetic as annealed and become lightly magnetic when cold worked.

Applications:
furnace parts, heating elements, heat exchangers, kiln liners, boiler baffles, auto exhaust parts; refinery, chemical and food processing equipment

bebon is a 310s stainless steel supplier in China, more information about 310s stainless steel,please see the following:

Grade 310S stainless steel is superior than 304 or 309 stainless steel in most environments, because it has high nickel and chromium content. It has high corrosion resistance and strength in temperatures up to 1149°C (2100°F). The following datasheet gives more details about grade 310S stainless steel.

Grade 310S stainless steel can be machined similar to that of grade 304 stainless steel.

Grade 310S stainless steel can be hot worked after heating at 1177°C (2150°F). It should not be forged below 982°C (1800°F). It is rapidly cooled to increase the corrosion resistance.

Grade 310S stainless steel can be welded using fusion or resistance welding techniques. Oxyacetylene welding method is not preferred for welding this alloy.

Grade 310S stainless steel does not react to heat treatment. Strength and hardness of this alloy can be increased by cold working.