Direct Sale Alloy 304/304H in China

Alloy 304/304H is hot selling in China. Alloy 304/304H is available in plates, sheets, bars and pipes. Welcome to inquiry. Bebon will supply direct sale Alloy 304/304H plates with high quality. \
Alloy 304/304H (UNS S30400/ S30409) is a modification of the most widely utilized "18-8" chromium-nickel austenitic stainless steel.
Corrosion Resistance:
Alloy 304/304H has good resistance to atmospheric corrosion, foods and beverages and to many organic and inorganic chemicals in moderately oxidizing to moderately reducing environments. The high chromium content of the alloy provides resistance to oxidizing solutions such as nitric acid up to 55% weight and up to 176°F (80°C).
Alloy 304/304H also resists moderately aggressive organic acids such as acetic. The nickel present in the alloy provides resistance to moderately reducing solutions such as pure phosphoric acid, whatever the concentration, in cold solutions and up to 10% diluted hot solutions. The alloy can also operate successfully in caustic solutions free of chlorides or fluorides at moderate temperatures.
Alloy 304/304H does not perform well in more highly reducing environments such as those containing chlorides and sulfuric acid.
Alloy 304/304H grades perform well in fresh water service with low levels of chlorides (less than 100ppm). At higher chloride levels the grade is susceptible to crevice corrosion and pitting. For successful performance under these more severe conditions, higher molybdenum content is need such as 316/316L. Alloy 304/304H is not recommended for service in marine environments.
Fabrication Data
Alloy 304/304H can be easily welded and processed by standard shop fabrication practices.
Welding:
Alloy 304/304H can be readily welded by most standard processes. After welding Alloy 304/304H it may be necessary to anneal the plate to restore the corrosion resistance lost by sensitization to intergranular corrosion when chromium carbides precipitate in the grain boundaries in the weld heat-affected zone.
Machining:
Alloy 304/304H is subject to work hardening during deformation and is subject to chip breaking. The best machining results are achieved with slower speeds, heavier feeds, excellent lubrication, sharp tooling and powerful rigid equipment.